eSun ePLA-Silk Mystic Filament 1.75mm 1kg Spool

eSun ePLA-Silk Mystic Filament 1.75mm 1kg Spool - Digitmakers.ca
eSun ePLA-Silk Mystic Filament 1.75mm 1kg Spool - Digitmakers.ca
eSun ePLA-Silk Mystic Filament 1.75mm 1kg Spool - Digitmakers.ca
eSun ePLA-Silk Mystic Filament 1.75mm 1kg Spool - Digitmakers.ca
screen may slightly differ with real color
Color:
Blue Orange Green

Product variant with selected options does not exist!

View all options as a list

Sale price
$29.99
Regular price
$39.99

Frequently Bought Together

In stock and ready for shipping

Three colors in One-line, this silk pla filament’s rich color matching makes the printed model full of mystery. You can observe the rich color combination performance from different angles of multi color pla filament.

Description:

The Multi color pla filament will bring you a wonderful dynamic sense through the three-color interlaced gradient. With the silk luster texture, ePLA-Silk Mystic's surface is smooth and does not show layer patterns; The silk pla filament is easy peel off, smooth and flat.


Selling point

Mystery Three-color
Silk glossy texture
Smooth surface

Easy to peel off
Excellent printability
Not easy to break

View more about PLA Filament

 

 

It can use with the eBOX Lite to keep the filament smoothly feeding to avoid twisting; Reduce the hanging angle structure in the model or reduce the speed for better cooling.

Parameter Information

Filament Properties Table
3D PRINTING FILAMENT ePLA-Silk Mystic
Density(g/cm3) 1.256
Heat Distortion Temp(℃,0.45MPa) 54.7
Melt Flow Index(g/10min) 11.32(190℃/2.16kg)
Tensile Strength(MPa) 57.64
Elongation at Break(%) 21.76
Flexural Strength(MPa) 78.70
Flexural Modulus(MPa) 2800.36
IZOD Impact Strength(kJ/㎡) 6.45
Durability 4/10
Printability 9/10
Recommended printing parameters
Extruder Temperature(℃) 190 – 230℃
Recommended temperature:210℃
Bed temperature(℃)  45 – 60°C
Fan Speed  100%
Printing Speed  40 – 100mm/s
Heated Bed  Optional
Recommended Build Surfaces Masking paper, PVP solid glue, PEI