Bambu Lab PA6-CF Black 1.75mm - 500g/1kg
|
1kg | ||
|
|
500g |
Carbon Fiber Reinforced PA6 (Nylon 6)
Product Features
- Superior Strength and Stiffness
- Toughness & Vibration Resistance
- Exceptional Thermal Resistance
- Comes with High Temperature Reusable Spool
- Diameter: 1.75mm +/- 0.03mm
Cautions for Use
- 0.2 mm Nozzle Not Compatible
- Stainless Steel Nozzle Not Recommended
- Dry before Use for the Highest Print Quality
- AMS NOT Compatible
Bambu PA6-CF is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly high stiffness and strength properties in dry environments and maintains exceptional heat resistance and impact resistance. Similar to other Bambu CF Filaments, these outstanding mechanical properties make it an ideal choice for printing fixtures, clamps, automotive and mechanical components and various structural and engineering parts that used in dry environments.
| Normal PA-CF | PA6-CF | Improved % | |
| Strength (Bending Strength - XY, dry state) | 128 MPa | 151 MPa | 18% |
| Stiffness (Bending Modulus - XY, dry state) | 4420 MPa | 5460 MPa | 24% |
Impact & Vibration Resistance
Bambu PA6-CF offers excellent impact resistance, ensuring effective vibration resistance for your prints. It is commonly used to print models that need to withstand impact, collision, and vibration.
Exceptional Thermal Resistance
| Filament | PLA Basic | PETG Basic | ABS | ASA | PC | PA6-CF | PAHT-CF | PET-CF |
| Heat Deflection Temperature / ℃ (0.45 MPa) | 57 ℃ | 69 ℃ | 87 ℃ | 100 ℃ | 117 ℃ | 186 ℃ | 194 ℃ | 205 ℃ |
Accessory Compatibility
| Recommended | Not Recommended | |
| Build Plate | Engineering Plate, High Temperature Plate or Textured PEI Plate | Cool Plate |
| Hotend | Hardened Steel 0.4 / 0.6 (recommended) / 0.8 mm | Hotend with Stainless Steel Nozzle (all size) Hotend with Hardened Steel Nozzle (0.2 mm) |
| Glue | Glue Stick Bambu Liquid Glue |
/ |
Recommended Printing Settings
| Drying Settings before Printing | 80 °C, 8 - 12 h |
| Printing and Keeping Container's Humidity | < 20% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 260 - 290 °C |
| Bed Temperature (with Glue) | 80 - 100 °C |
| Printing Speed | < 100 mm/s |
Physical Properties
| Density | 1.09 g/cm³ |
| Vicat Softening Temperature | 212 °C |
| Heat Deflection Temperature | 186 °C |
| Melting Temperature | 223 °C |
| Melt Index | 6.8 ± 0.6 g/10 min |
Mechanical Properties
| Tensile Strength | 102 ± 7 MPa |
| Breaking Elongation Rate | 5.8 ± 1.6 % |
| Bending Modulus | 5460 ± 280 MPa |
| Bending Strength | 151 ± 8 MPa |
| Impact Strength | 40.3 ± 2.5 kJ/m² |
Printing Tips
• Drying conditions: 80℃ for 10 hrs. PA6-CF is highly sensitive to humidity. To achieve optimal printing performance, it is recommeded further drying before use and after storage. For more details please refer to: Filament drying instructions on WIKI.
• Bambu PA6-CF will experience a decrease in strength and stiffness after absorbing water,making it not recommended for printing models with high requirements for strength, stiffness, and dimensional stability, especially thin and elongated models. The prints of PA6-CF usually become tougher and more resistant to impacts, drops, and collisions when they get damp, you can dampen and soften the prints in advance if the model requires high toughness.
• When printing a model with support, it is necessary to remove the support structure within 2 hours to prevent it from being difficult to remove after being damp and softened. Please dry the prints and let them cool down if it is difficult to remove the support, and then remove the support in time.
• Fully impregnating the surface of the prints with paint, wax and other water-proof coatings can inhibit water absorption and prevent them from becoming soft.